BGGF-10 Cat Serpihan Kaca Epoksi Kaca

Deskripsi

Deskripsi Produk:

This product is a ​​two-component, high-solids epoxy coating​​ reinforced with ​​glass flake pigments​​, offering exceptional durability and corrosion resistance.

Main Features:

This product is suitable for steel structures exposed to severe environments with both atmospheric corrosion and mechanical wear. It offers excellent anti-corrosion and wear-resistant properties. It is used for the protection of steel structures in various corrosive environments, including splash zones of offshore structures, decks, and waterfront areas, pile structures, pulp mills, bridges, and chemical plants.

Parameter Fisik:

• Color: Limited
• Volume Solids: 75±2%
• Standard Dry Film Thickness: Dry Film: 200 microns Wet Film: 267 microns
• Theoretical Coverage Rate: 2.6 m²/kg, 3.75 m²/L (based on 200 microns dry film)
• Actual Coverage Rate: Considering appropriate loss factor
• Flash Point: 28±2°C

Petunjuk Aplikasi:

Persiapan Permukaan:

The performance of this product depends on the extent of surface preparation. The surface to be painted must be clean, dry, and free from contaminants. Before applying the paint, all surfaces should be assessed and treated in accordance with ISO 8504:2000 standards. Accumulated dirt and soluble salts must be removed. Dirt can typically be removed with a dry brush. Soluble salts should be removed through freshwater rinsing.

Oil and grease should be removed in accordance with the SSPC-SP1 solvent cleaning standard.

Sandblasting should be carried out to Sa2.5 (ISO 8501-1:2007) or SSPC-SP6 standards. If oxidation occurs on the surface between sandblasting and the application of this product, the surface should be re-blasted to meet the specified standards.

Surface defects exposed during sandblasting should be ground, filled, or addressed using appropriate methods. A recommended surface roughness is 50-70 microns.

The substrate temperature should not be lower than 10°C, and it should be at least 3°C higher than the dew point temperature.

Pencampuran:

This product is supplied in two containers, forming one unit. It must be mixed in pairs according to the specified ratio each time and used up within the prescribed mixing and use period.

1. Mix the base (Component A) with a mechanical stirrer.
2. Thoroughly mix all the curing agent (Component B) with the base (Component A) using a mechanical stirrer.

Mixing and Use Period:

• 15℃	25℃	35℃
  4H	2H	1H

Lebih tipis: BTE Thinner

Metode Aplikasi: Airless Spray Air Spray (with a pressure pot) Brush Application / Roller Application (for small areas only)

Rasio Penipisan:

• Metode konstruksi:	airless spray	air spray (with pressure tank)	brush/roller
  Dilution ratio:	0-5%	5-20%	0-10%

Semprotan Tanpa Udara:

Nozzle Size: 0.63-1.09mm Spray Pressure: 15 MPa

Waktu Pengeringan:

Recoating Interval: (with this product as the recoat)

Note: The above data is for guidance only. Actual drying and recoat times can vary depending on film thickness, ventilation, humidity, underlying paint, early loading/unloading requirements, and mechanical strength, among other factors.

This product is suitable for underwater and outdoor atmospheric environments. For underwater applications, a minimum paint system thickness of 450 microns is required for long-lasting corrosion protection. For general outdoor atmospheric exposure, a minimum paint system thickness of 350 microns is required. Airless spray application provides the highest film thickness in a single coat. With other application methods, the required film thickness cannot be achieved. For air spray application to reach the maximum film thickness, multiple cross coats are necessary. When applying this product by brush or roller, multiple coating layers are required to reach the specified total dry film thickness.

Pembersihan Alat: Clean all tools with BTE Thinner after use.

Spesifikasi Kemasan:

25kg per set

Periode Penyimpanan:

In a cool, dry, and shaded area, the unopened storage life is one year (at 25°C).